Failures of steel parts in service or production occur very infrequently. However, when steel parts fail, the consequences are dire.
Here are 7 ways that steel can fail as a result of Quench Cracking from heat treatment.
- Overheating during the austenitizing portion of the heat treatment cycle can coarsen normally fine grained steels. coarse grained steels increase hardening depth and are more prone to quench cracking than fine grain steels. Avoid over heating and overly long dwell times while austenitizing.
- Improper quenchant. Yes, water, brine, or caustic will get the steel “harder.” If the steel is an oil hardening steel, the use of these overly aggressive quenchants will lead to cracking.
- Improper selection of steel for the process.
- Too much time between the quenching and the tempering of the heat treated parts. A common misconception is that quench cracks can occur only while the piece is being quenched. This is not true. If the work is not tempered right away, quench cracks can (and will) occur.
- Improper design– Sharp changes of section, lack of radii, holes, sharp keyways, unbalanced sectional mass, and other stress risers.
- Improper entry of the part/ delivery of the quenchant to the part. Differences in cooling rates can be created, for example, if parts are massed together in a basket resulting in the parts along the edges cooling faster than those in the mass in the center. Part geometry can also interfere with quenchant delivery and effectiveness, especially on induction lines.
- Failure to take sufficient stock removal from the original part during machining. This can leave remnants of seams or other surface imperfections which can act as a nucleation site for a quench crack.
Finally, materials that are heat treated to very high strength levels, even though they did not quench crack, may contain localized concentrations of high residual stresses. If these stresses are acting in the same direction as the load applied in service, an instantaneous failure can occur. This will be virtually indistinguishable from a quench crack during an examination, due to its brittle failure mode, lack of decarburization on surface of the fracture, or other forensic evidence of a process failure.
When looking at quench cracking failures under the microscope, cracks and crack tributaries that follow the prior austenitic grain boundaries are a pretty good clue that grain coarsening and or its causes- overheating or too long time at temperature- occurred. Temper scale on the fracture surface helps the metallurgist know that the crack was present before tempering. Decarburization may show that the crack was open prior to quenching.
Photo1 Thanks to WIP SAMI over at British Blades for the photo.
Bill Fedun says:
Milo, I have linked to this article from my armour making blog site. FYI.
http://southtowerarmouringguild.blogspot.com
Thank you for the great articles!
—-stag—
Bill Fedun says:
Oh, heres a real error which needs fixing! You name is Miles, not Milo! I’ll fix that. (what WAS I thinking!)
Regards,
—-stag—-
speakingofprecision says:
Well, I was just warming up on CR 4 for a few years to get my wings…
Regards.
speakingofprecision says:
Well, I was just warming up on CR 4 for a few years to get my wings…
Regards.
speakingofprecision says:
Thank you for the link and support.
Miles
speakingofprecision says:
Thank you for the link and support.
Miles
Dhanithraj A V says:
We are getting cracks in EN 8 bars after induction hardening,,,.. can i know the reasons behind this cracks
Dhanithraj A V says:
We are getting cracks in EN 8 bars after induction hardening,,,.. can i know the reasons behind this cracks
speakingofprecision says:
EN 8 is nominal equivalent of US grade 1040. You do not specify the diameter of the bar, the depth of the hardness, nor the quenchant. you do not provide the frequency, depth, or time.involved. You do not specify if there is a temper cycle after quenching. You do not specify if the cracks are longitudinal, or transverse.
It is possible that the cracking is being initiated on a prior existing seam, you do not inform us if the bars are black (as rolled) or Have had stock removal taken prior to induction process.
Have you done any metallography on the cracks? what do you see? any evidence of decarburization? Scale?
Failure analysis is a matter of asking the appropriate questions that identify which of the precondiditions for the failure were present, and eliminating as probable cause those that were not.
speakingofprecision says:
EN 8 is nominal equivalent of US grade 1040. You do not specify the diameter of the bar, the depth of the hardness, nor the quenchant. you do not provide the frequency, depth, or time.involved. You do not specify if there is a temper cycle after quenching. You do not specify if the cracks are longitudinal, or transverse.
It is possible that the cracking is being initiated on a prior existing seam, you do not inform us if the bars are black (as rolled) or Have had stock removal taken prior to induction process.
Have you done any metallography on the cracks? what do you see? any evidence of decarburization? Scale?
Failure analysis is a matter of asking the appropriate questions that identify which of the precondiditions for the failure were present, and eliminating as probable cause those that were not.
S J Kamath says:
Had similar problem cracks in the induction hardening of crank pins of crankshaft which was due to higher range of hardenability in the steel used. This was resolved by reducing the severity of quenching by increasing the concentration of polymer quenchant.
S J Kamath says:
Had similar problem cracks in the induction hardening of crank pins of crankshaft which was due to higher range of hardenability in the steel used. This was resolved by reducing the severity of quenching by increasing the concentration of polymer quenchant.
Varun Mishra says:
Sir, I work in JSW steel ltd., can u please end me more information about surface defects of CRCA, HRPO and HRSPO. Their causes and their identity?
I would be really grateful.
Thanks & Regards,
Varun Mishra
moc.oohay@777arhsim_nurav
Varun Mishra says:
Sir, I work in JSW steel ltd., can u please end me more information about surface defects of CRCA, HRPO and HRSPO. Their causes and their identity?
I would be really grateful.
Thanks & Regards,
Varun Mishra
moc.oohay@777arhsim_nurav
lee hyeck says:
Hellow i`m south korean university student.
i impressed “cause metal crack”
i` want you solution
my question is…..
how can metal crack reduce??
Thanks you
lee hyeck says:
Hellow i`m south korean university student.
i impressed “cause metal crack”
i` want you solution
my question is…..
how can metal crack reduce??
Thanks you
Dan Hoiuston says:
The link below shows cracking in the inside corner of a shelf projrction of a massive steel anvil casting. The anvil is of German manufacture and is generally considered to be a top of the line product with working surfaces hardened to rockwell 59 hardness to a depth of 1inch.
My question is can these cracks be expected to continue to propogate through the casting body or will they be likely to be contained/stopped by the underlying unhardened body of the anvil casting.
Can other effects of these cracks be predicted ?
http://www.iforgeiron.com/topic/39406-purchasing-a-new-anvil/
Dan Hoiuston says:
The link below shows cracking in the inside corner of a shelf projrction of a massive steel anvil casting. The anvil is of German manufacture and is generally considered to be a top of the line product with working surfaces hardened to rockwell 59 hardness to a depth of 1inch.
My question is can these cracks be expected to continue to propogate through the casting body or will they be likely to be contained/stopped by the underlying unhardened body of the anvil casting.
Can other effects of these cracks be predicted ?
http://www.iforgeiron.com/topic/39406-purchasing-a-new-anvil/
suresh bahadur singh says:
Mat En-8D Dia-15mm Quenchig crack U shape on Milling Operation thickness near hole
suresh bahadur singh says:
Mat En-8D Dia-15mm Quenchig crack U shape on Milling Operation thickness near hole
suresh bahadur singh says:
Quenching Crack During Induction Hardening Mat-En8D Dia19mm bar Witween Flat Milling &5mm Dia Hole,Wetween Flat Milling & Hole Thickness 2mm Quenching in Water Mixed 3% Polymor Case Depth-1.8 mm Machie Power-52.5
suresh bahadur singh says:
Quenching Crack During Induction Hardening Mat-En8D Dia19mm bar Witween Flat Milling &5mm Dia Hole,Wetween Flat Milling & Hole Thickness 2mm Quenching in Water Mixed 3% Polymor Case Depth-1.8 mm Machie Power-52.5
speakingofprecision says:
Cracks will continue to grow until all stresses are equalized. And with repeated cyclic heating and working, It is not even worth trying to repair by welding.
Scrap.
speakingofprecision says:
Cracks will continue to grow until all stresses are equalized. And with repeated cyclic heating and working, It is not even worth trying to repair by welding.
Scrap.
speakingofprecision says:
Section changes are often the location for quench cracking.
speakingofprecision says:
Section changes are often the location for quench cracking.
Hassan ahmed Hassan says:
I am steel plant manager in KSA. I have longitudinal cracks in 16 mm reinforcement bar.
Hassan ahmed Hassan says:
I am steel plant manager in KSA. I have longitudinal cracks in 16 mm reinforcement bar.
speakingofprecision says:
https://pmpaspeakingofprecision.com/2012/05/24/seams-on-rolled-steel-products/
Here you go.
speakingofprecision says:
https://pmpaspeakingofprecision.com/2012/05/24/seams-on-rolled-steel-products/
Here you go.
Volwnz says:
purchase lasuna online – cheap diarex generic order himcolin generic